Z240g Heavily Galvanized Hot Dip Galvanized Steel Wire With Gabion
Box
Hot Dip Galvanized Steel Wire Specification
Hot dip galvanized steel wire made of high quality low carbon
steel, it is processed through drawing, pickling, rust removal,
high-temperature annealing, hot-dip galvanized, and cooling.Hot dip
galvanized steel wire is also known as hot dipped galvanized wire
or thermal galvanized wire. It is made by mean of wire drawing
followed by heat treatment and zinc plating. Wire Materials: Iron
wire, carbon steel wire. Advantages: Excellent flexibility and
softness.
Hot Dip Galvanized Steel Wire Technology
Hot dip galvanized steel wire made of high-quality low-carbon steel
Surface Treatment:
Electro galvanized(Cold galvanized wire)3-6M (Zinc coated 8-15g/m2)
Hot dipped galvanized wire (Zinc Coated 40-60g/m2)
Heavily galvanized wire (Zinc Coated more than 240g/m2)
Zinc aluminum alloy (Golfan)
(5%aluminum+95%zinc)(10%aluminum+90%zinc)95Zn-5Al-MM
(Zinc coated more than 240g/m2) Generally used as gabion mesh
weaving material.
Hot Dip Galvanized Steel Wire Application
Hot dip galvanized steel wire application:
Because the resulting coating is thicker, hot dip galvanized steel
wire has better protective properties than electro galvanized iron
wire, so it is an important protective coating for steel parts used
in harsh working environments. Hot dip galvanized steel wire
products are widely used in chemical equipment, petroleum
processing, ocean exploration, metal structures, power
transmission, shipbuilding and other industries. They are also used
in agricultural fields such as pesticide sprinkler irrigation,
greenhouses, and construction industries such as water and gas
transmission, wire casings, scaffolding, and bridges,highway
guardrails, etc.They have been widely used in recent years.
Hot Dip Galvanized Steel Wire Features
1. Durability: hot-dip galvanized steel wire can be maintained for
more than 30 years without repair.
2. Good reliability: The galvanized layer is combined with the
metallurgy of the steel and becomes part of the surface of the
steel, making the coating reliable.
3. Strong coating toughness: The galvanized layer of galvanized
wire forms a special metallographic structure and can withstand
mechanical damage during transportation and use.
4. Comprehensive protection: Every part of the galvanized wire can
be galvanized, even depressions and sharp corners can be fully
protected.
Hot Dip Galvanized Steel Wire Parameter:
| Product Name | Hot Dip Heavily Galvanized Steel Wire |
| Material | Low carbon steel Q195 |
| Diameter | BWG5-BWG24 |
| Zinc Rate | 240g/m2 |
| Tensile Strength | 350-550/mm2 |
| Elongation Rate | 10%-25% |
| Weight/Coil | 0.1kg-1000kgs/coil |
| Packing | 1.Plastic inside and hessian outside ;
2.Plastic inside and nylon woven outside. 3.As your request. |
Hot Dip Galvanized Steel Wire Size:
| Wire Gauge Size | SWG(mm) | BWG(mm) | metric(mm) |
| 8 | 4.06 | 4.19 | 4.00 |
| 9 | 3.66 | 3.76 | - |
| 10 | 3.25 | 3.40 | 3.50 |
| 11 | 2.95 | 3.05 | 3.00 |
| 12 | 2.64 | 2.77 | 2.80 |
| 13 | 2.34 | 2.41 | 2.50 |
| 14 | 2.03 | 2.11 | - |
| 15 | 1.83 | 1.83 | 1.80 |
| 16 | 1.63 | 1.65 | 1.65 |
| 17 | 1.42 | 1.47 | 1.40 |
| 18 | 1.22 | 1.25 | 1.20 |
| 19 | 1.02 | 1.07 | 1.00 |
| 20 | 0.91 | 0.89 | 0.90 |
| 21 | 0.81 | 0.813 | 0.80 |
| 22 | 0.71 | 0.711 | 0.70 |
Hot Dip Galvanized Steel Wire Pictures: